• This structure was discovered by Wörle and Nesper in 1994. They billed it as

``A New Graphite-Related Refractory Compound''

As such, we've moved it into the sp2 section of the Carbon and Related Structures page.

• Prototype: MgB2C2
• Pearson Symbol: oC80
• Space Group: Cmca (Cartesian and lattice coordinate listings available)
• Number: 64
• Primitive Vectors:  A1 = ½ a X - ½ b Y A2 = ½ a X + ½ b Y A3 = c Z
• Basis Vectors:  B1 = + x1 A1 + x1 A2 = + x1 a X (MgI) (8d) B2 = - x1 A1 - x1 A2 = - x1 a X (MgI) (8d) B3 = - (½ + x1) A1 + (½ - x1) A2 + ½ A3 = - x1 a X + ½ b Y + ½ c Z (MgI) (8d) B4 = - (½ - x1) A1 + (½ + x1) A2 + ½ A3 = - x1 a X + ½ b Y + ½ c Z (MgI) (8d) B5 = - y2 A1 + y2 A2 + z2 A3 = + y2 b Y + z2 c Z (MgII) (8f) B6 = + y2 A1 - y2 A2 - z2 A3 = - y2 b Y - z2 c Z (MgII) (8f) B7 = - (½ - y2) A1 + (½ - y2) A2 + (½ + z2) A3 = + (½ - y2) b Y + (½ + z2) c Z (MgII) (8f) B8 = - (½ + y2) A1 + (½ + y2) A2 + (½ - z2) A3 = + (½ + y2) b Y + (½ - z2) c Z (MgII) (8f) B9 = + (¼ - y3) A1 + (¼ + y3) A2 + ¼ A3 = + ¼ a X + y3 b Y + ¼ c Z (BI) (8e) B10 = + (¾ + y3) A1 + (¾ - y3) A2 + ¾ A3 = + ¾ a X - y3 b Y + ¾ c Z (BI) (8e) B11 = + (¼ + y3) A1 + (¼ - y3) A2 + ¾ A3 = + ¼ a X - y3 b Y + ¾ c Z (BI) (8e) B12 = + (¾ - y3) A1 + (¾ + y3) A2 + ¼ A3 = + ¾ a X + y3 b Y + ¼ c Z (BI) (8e) B13 = - y4 A1 + y4 A2 + z4 A3 = + y4 b Y + z4 c Z (BII) (8f) B14 = + y4 A1 - y4 A2 - z4 A3 = - y4 b Y - z4 c Z (BII) (8f) B15 = - (½ - y4) A1 + (½ - y4) A2 + (½ + z4) A3 = + (½ - y4) b Y + (½ + z4) c Z (BII) (8f) B16 = - (½ + y4) A1 + (½ + y4) A2 + (½ - z4) A3 = + (½ + y4) b Y + (½ - z4) c Z (BII) (8f) B17 = + (x5 - y5) A1 + (x5 + y5) A2 + z5 A3 = + x5 a X + y5 b Y + z5 c Z (BIII) (16g) B18 = + (y5 - x5) A1 - (x5 + y5) A2 - z5 A3 = - x5 a X - y5 b Y - z5 c Z (BIII) (16g) B19 = - (½ + x5 - y5) A1 + (½ - x5 - y5) A2 + (½ + z5) A3 = - x5 a X + (½ - y5) b Y + (½ + z5) c Z (BIII) (16g) B20 = - (½ - x5 + y5) A1 + (½ + x5 + y5) A2 + (½ - z5) A3 = + x5 a X + (½ + y5) b Y + (½ - z5) c Z (BIII) (16g) B21 = - (½ + x5 + y5) A1 + (½ - x5 + y5) A2 + (½ - z5) A3 = - x5 a X + (½ + y5) b Y + (½ - z5) c Z (BIII) (16g) B22 = - (½ - x5 - y5) A1 + (½ + x5 - y5) A2 + (½ + z5) A3 = + x5 a X + (½ - y5) b Y + (½ + z5) c Z (BIII) (16g) B23 = + (x5 + y5) A1 + (x5 - y5) A2 - z5 A3 = + x5 a X - y5 b Y - z5 c Z (BIII) (16g) B24 = - (x5 + y5) A1 + (y5 - x5) A2 + z5 A3 = - x5 a X + y5 b Y + z5 c Z (BIII) (16g) B25 = + (¼ - y6) A1 + (¼ + y6) A2 + ¼ A3 = + ¼ a X + y6 b Y + ¼ c Z (CI) (8e) B26 = + (¾ + y6) A1 + (¾ - y6) A2 + ¾ A3 = + ¾ a X - y6 b Y + ¾ c Z (CI) (8e) B27 = + (¼ + y6) A1 + (¼ - y6) A2 + ¾ A3 = + ¼ a X - y6 b Y + ¾ c Z (CI) (8e) B28 = + (¾ - y6) A1 + (¾ + y6) A2 + ¼ A3 = + ¾ a X + y6 b Y + ¼ c Z (CI) (8e) B29 = - y7 A1 + y7 A2 + z7 A3 = + y7 b Y + z7 c Z (CII) (8f) B30 = + y7 A1 - y7 A2 - z7 A3 = - y7 b Y - z7 c Z (CII) (8f) B31 = - (½ - y7) A1 + (½ - y7) A2 + (½ + z7) A3 = + (½ - y7) b Y + (½ + z7) c Z (CII) (8f) B32 = - (½ + y7) A1 + (½ + y7) A2 + (½ - z7) A3 = + (½ + y7) b Y + (½ - z7) c Z (CII) (8f) B33 = + (x8 - y8) A1 + (x8 + y8) A2 + z8 A3 = + x8 a X + y8 b Y + z8 c Z (CIII) (16g) B34 = + (y8 - x8) A1 - (x8 + y8) A2 - z8 A3 = - x8 a X - y8 b Y - z8 c Z (CIII) (16g) B35 = - (½ + x8 - y8) A1 + (½ - x8 - y8) A2 + (½ + z8) A3 = - x8 a X + (½ - y8) b Y + (½ + z8) c Z (CIII) (16g) B36 = - (½ - x8 + y8) A1 + (½ + x8 + y8) A2 + (½ - z8) A3 = + x8 a X + (½ + y8) b Y + (½ - z8) c Z (CIII) (16g) B37 = - (½ + x8 + y8) A1 + (½ - x8 + y8) A2 + (½ - z8) A3 = - x8 a X + (½ + y8) b Y + (½ - z8) c Z (CIII) (16g) B38 = - (½ - x8 - y8) A1 + (½ + x8 - y8) A2 + (½ + z8) A3 = + x8 a X + (½ - y8) b Y + (½ + z8) c Z (CIII) (16g) B39 = + (x8 + y8) A1 + (x8 - y8) A2 - z8 A3 = + x8 a X - y8 b Y - z8 c Z (CIII) (16g) B40 = - (x8 + y8) A1 + (y8 - x8) A2 + z8 A3 = - x8 a X + y8 b Y + z8 c Z (CIII) (16g)