Crystal Lattice Structures: Creation Date: 19 Feb 2003 Last Modified: 21 Oct 2004

The CuSbS2 (F56) Structure

You can now

• Prototype: CuSbS2
• Pearson Symbol: oP16
• Strukturbericht Designation: F56
• Space Group: Pnma (Cartesian and lattice coordinate listings available)
• Number: 62
• Reference: Strukturbericht, Vol III, p. 75.
• Primitive Vectors:  A1 = a X A2 = b Y A3 = c Z
• Basis Vectors:  B1 = + x1 A1 + ¼ A2 + z1 A3 = + x1 a Y + ¼ b Y + z1 c Z (Cu) (4c) B2 = + (½ + x1) A1 + ¼ A2 + (½ - z1) A3 = + (½ + x1) a Y + ¼ b Y + (½ - z1) c Z (Cu) (4c) B3 = - x1 A1 - ¼ A2 - z1 A3 = - x1 a Y - ¼ b Y - z1 c Z (Cu) (4c) B4 = + (½ - x1) A1 - ¼ A2 + (½ + z1) A3 = + (½ - x1) a Y - ¼ b Y + (½ + z1) c Z (Cu) (4c) B5 = + x2 A1 + ¼ A2 + z2 A3 = + x2 a Y + ¼ b Y + z2 c Z (Sb) (4c) B6 = + (½ + x2) A1 + ¼ A2 + (½ - z2) A3 = + (½ + x2) a Y + ¼ b Y + (½ - z2) c Z (Sb) (4c) B7 = - x2 A1 - ¼ A2 - z2 A3 = - x2 a Y - ¼ b Y - z2 c Z (Sb) (4c) B8 = + (½ - x2) A1 - ¼ A2 + (½ + z2) A3 = + (½ - x2) a Y - ¼ b Y + (½ + z2) c Z (Sb) (4c) B9 = + x3 A1 + ¼ A2 + z3 A3 = + x3 a Y + ¼ b Y + z3 c Z (S-I) (4c) B10 = + (½ + x3) A1 + ¼ A2 + (½ - z3) A3 = + (½ + x3) a Y + ¼ b Y + (½ - z3) c Z (S-I) (4c) B11 = - x3 A1 - ¼ A2 - z3 A3 = - x3 a Y - ¼ b Y - z3 c Z (S-I) (4c) B12 = + (½ - x3) A1 - ¼ A2 + (½ + z3) A3 = + (½ - x3) a Y - ¼ b Y + (½ + z3) c Z (S-I) (4c) B13 = + x4 A1 + ¼ A2 + z4 A3 = + x4 a Y + ¼ b Y + z4 c Z (S-II) (4c) B14 = + (½ + x4) A1 + ¼ A2 + (½ - z4) A3 = + (½ + x4) a Y + ¼ b Y + (½ - z4) c Z (S-II) (4c) B15 = - x4 A1 - ¼ A2 - z4 A3 = - x4 a Y - ¼ b Y - z4 c Z (S-II) (4c) B16 = + (½ - x4) A1 - ¼ A2 + (½ + z4) A3 = + (½ - x4) a Y - ¼ b Y + (½ + z4) c Z (S-II) (4c)

Go back to the Sulfur and Its Compounds page.

Go back to Crystal Lattice Structure page.

 Structures indexed by: This is a mirror of an old page created at theNaval Research LaboratoryCenter for Computational Materials ScienceThe maintained successor is hosted at http://www.aflowlib.org/CrystalDatabase/ and published as M. Mehl et al., Comput. Mater. Sci. 136 (Supp.), S1-S828 (2017).